Ni60A
Features:
High purity, high hardness, wear resistance and corrosion resistance, low friction coefficient, excellent self-melting, wettability and spray welding, high sphericity, low oxygen, smooth surface, uniform particle size distribution, excellent flow properti
Application:
Packing:
Precision grinding, intelligent manufacturing technology, integrated solutions
Aluminum foil bag, iron drum, plastic drum, woven bag, pallet, customized packaging
Date of delivery:
Precision grinding, intelligent manufacturing technology, integrated solutions
3-15 days
key word:
Chemical composition（wt%）
【化学成分Chemical Composition】
|
牌号 Code |
Cr |
B |
Si |
Fe |
C |
Others |
Ni |
|
Ni60A |
14.0-17.0 |
2.5-3.5 |
4.0-5.0 |
≤5 |
0.6-1.0 |
≤1 |
Bal |
Physical indicators
【物理性能表Physical property table】
|
粉末规格 |
氧含量 |
松装密度 |
卡尼流速 |
硬度 |
工作温度 |
|
45-125μm |
≤0.03 |
4.22 |
＜17 |
HRC58-60 |
≤650°C |
Application areas
Parts repair
Plasma spray welding
Laser Cladding
Recommend products
BNi-2 is one of the most widely used nickel-based brazing alloys, characterized by a low melting temperature, good wettability, and fluidity. During the brazing process, the base material grains do not grow, which helps prevent deterioration of component performance.
View Details
1. High-Temperature and Corrosion Resistance Temperature range: -200°C to 1000°C, oxidation and sulfidation corrosion resistance. Resistant to seawater, chlorides, and acidic media corrosion, suitable for marine and chemical environments. 2. Excellent Processability High sphericity (≥98%), low oxygen content (≤0.1%), good fluidity, reducing 3D printing defects. Strong bonding strength with the substrate, supporting the formation of high-precision complex structures. 3. High Strength and Toughness Room temperature tensile strength ≥900 MPa, maintaining excellent mechanical properties at high temperatures.
View Details
1. High-Temperature Performance Applicable temperature range: -250°C to 700°C, resistant to high-temperature oxidation, creep, and sulfide corrosion. Strength is significantly improved after age hardening (room temperature tensile strength ≥ 1300 MPa). 2. Corrosion Resistance Resistant to acids, alkalis, chlorides, and seawater corrosion, suitable for chemical, marine, and nuclear industries. 3. Process Compatibility High sphericity (≥97%), low oxygen content (≤0.1%), excellent fluidity, compatible with additive manufacturing processes such as SLM (Selective Laser Melting) and EBM (Electron Beam Melting). No tendency for cracking after welding, supports the precision forming of complex structures.
View Details
The carbon and boron in BNi-1 brazing filler metal can diffuse into the base material during the brazing process, thereby increasing the remelting temperature of the brazed joint. This filler metal has a high chromium content, so the brazed joint exhibits good high-temperature performance and is suitable for components subjected to high stress at elevated temperatures.
View DetailsMaybe you want to know something else.
Contact Us
Address: No.39, Liandong Yougu lnd. Park, Bachelor Street,Changsha City,Hunan Province, China.